KTP

The dielectric constant ε₂₂ of KTP varies little with frequency and is not affected by the electric coupling effect under pressure. ε₃₃ varies greatly with frequency and is not affected by the electrical coupling effect under pressure. Especially at high frequencies, ε₂₂ and ε₃₃ do not vary with frequency.Outside the 500kHz-10MHz region, electro-optic devices made with KTP crystals do not produce parasitic oscillations due to piezoelectric coupling, which are severe in other electro-optic crystals. The thermal hysteresis effect of KTP is much smaller and has high temperature stability.​

Size(mm)	Θ, Φ	Coating	Application	Price	Delivery (week)	Order
3*3*5	90°, 23.5°	AR/AR@532+1064 nm	SHG@1064 nm, type II	120	1-2
3*3*10	90°, 23.6°	AR/AR@532+1064 nm	SHG@1064 nm, type II	140	1-2
5*5*5	90°, 23.7°	AR/AR@532+1064 nm	SHG@1064 nm, type II	210	1-2
5*5*10	90°, 23.8°	AR/AR@532+1064 nm	SHG@1064 nm, type II	300	1-2
7*7*5	90°, 23.9°	AR/AR@532+1064 nm	SHG@1064 nm, type II	350	1-2
7*7*10	90°, 23.10°	AR/AR@532+1064 nm	SHG@1064 nm, type II	470	1-2
3*3*5	-	AR/AR@1064 nm&533 nm	SHG@1064 nm, type II	Negotiable	1-2
3*3*10	-	AR/AR@1064 nm&534 nm	SHG@1064 nm, type II	Negotiable	1-2
7*7*20	-	AR@1064 nm&532 nm	OPO for 1064@1570 nm, type II	Negotiable	1-2
5*5*20	90°, -	AR/AR@1064+1570+3300 nm	X-cut for eye safe generation by OPO @ 1064 nm -> 1570 nm + 3300 nm	650	1-2
4.5*4.5*9	90°, 23.5°	AR/AR@1064+532 nm	SHG@1064 nm, type II	500	1-2